ceramic disc capacitor suntan ? class i temperature compensation TS15 f e a t u r e s ? linear temperature coefficient of capacitance. ? high stability of capacitance. ? low loss at wide ranfe of frequency. specifications operating temperature range -25 to +85 rated working voltage dc 50v, 500v test voltage 3 times of the rated voltage capacitance within the tolerance at 1 mhz, 1 0.2 vrms. 25 q factor at 1 mhz. 1 0.2 vrms. 25 c 30pf ??q 1 ,000 c<30pf ??q 400+20 (c: rated capacitance) insulation resistance 10,000 m ? min. capacitance dimensions (mm) rated volt. (vdc) temp. char. range (pf) tolerance d ? max t max f 0.5 ~ 47 5.5 50 ~ 75 6.5 82 ~ 100 7.5 120 ~ 150 8.5 180 ~ 270 10.5 5.0 50 ch 0 60 ppm/ (npo) 300 ~ 390 0.25pf & 0.5pf (under 10pf) 5% & 10% (over 10pf) 12.5 3.5 5.9, 10.0 10 ~ 120 5.5 150 ~ 240 6.5 270~ 330 7.5 360 ~ 470 8.5 50 sl +350 ~ -1000ppm/ 500 ~ 820 5% & 10% 10.5 3.5 5.0 class ii high dielec tric constant f e a t u r e s ? large capacitance in small sizes. ? non liner temperature coef ficient of capacitance. specifications rated working voltage dc 50v, 500v test voltage 2.5 times of the rated voltage capacitance within the tolerance at 1 mhz, 1 0.2 vrms. 25 dissipation factor (tan ) y5p, z5u : tan 2.5% z5v : tan 5% insulation resistance 10,000m ? or 200m ? f, whichever is the smaller capacitance dimensions (mm) rated volt. (vdc) temp. char. range (pf) tolerance d ? max t max f 100 ~ 2000 5.5 2200 . 2700 6.5 3000 . 3300 7.5 3900 . 4700 8.5 50 b 10% 5600 . 6800 10000 10% & 20% 10.5 3.5 5.0 2200 . 3300 4700 . 5000 5.5 5600 . 6800 8200 6.5 10000 7.5 12000 . 15000 8.5 50 e +22 ~ -56% (z5u) 18000 . 20000 22000 20% & +80-20% 10.5 3.5 5.0 4700 . 5000 5.5 10000 . 15000 6.5 18000 . 20000 7.5 22000 . 30000 8.5 50 f +22 ~ -82% (z5v) 33000 . 40000 +80-20% 10.5 3.5 5.0 note: specification are subject to change without notic e. for more detail and update, please visit our website. suntan ? technology company limited website: www.suntan.com.hk email: info@suntan.com.hk tel: (852) 8202 8782 fax: (852) 8208 6246
|